The application of metal dental restorations in oral prosthetics has become very widespread and popular. Due to the complexity of the intraoral environment, it has been the focus of research to improve the mechanical and chemical properties, especially the corrosion resistance, to increase the durability of restorations under the premise of ensuring the good biocompatibility of the materials.Haoka et al. tested the electrochemical properties of niobium-containing magnetic attachments, and the results showed that compared with the traditional magnetic attachments, the magnetic attachments made of Pt-30.0mass%Fe-0.6mass%Nb alloys had better corrosion resistance.Lee et al. tested the electrochemical properties of titanium-niobium alloys. Lee et al. tested the structural properties of titanium-niobium alloys and showed that Ti-10Nb and Ti-27.5Nb alloys had the highest strength, while Ot' phase-dominated (17.5Nb, 20Nb) alloys and B-phase-dominated alloys (>30Nb) の弾性率が最も低かった。 。 さらに、テストに参加したすべてのチタンニオブ合金は優れた耐食性を示しました。

菊池ら。 異なる比重のニオブを含む鋳造チタンニオブ合金の機械的特性をテストしたところ、5重量%のニオブを含むチタン合金の硬度が大幅に向上したことが結果からわかりました。 10重量%以上のニオブを含むチタン合金は、降伏強度と引張強度が大幅に向上しましたが、伸びは大幅に減少しました。 30 wt% のニオブを含むチタン合金は、より高い硬度、強度、弾性率を維持しながら、より優れた研磨特性を示しました。 Hu Xinらによる研究。 また、高強度、高弾性率のチタン・ジルコニウム・ニオブ・錫合金は口腔修復物として生体安全性に優れた金属材料であるが、表面荷重の増加に伴い摩耗機構が摩耗摩耗から粘着摩耗に変化することも確認した。